Construction applications: SUPERPLASTICIZERS are used to reduce water in CONCRETE formulations. specially formulated organic plasticizer improves the workability of concrete, reducing water requirement and making the concrete stronger. It retards the setting of concrete so that transportation of RMC is not a problem. Benefits of these additives include improved strength, improved workability, improved durability of cement mixtures. This polymer mixture in cement mixtures control air pore content and prevent AGGLOMERATION of powders during the spray-drying process from the powder manufacturing and storage. Coating formulations with RXSOL-67-6704-210 containing polymers prevent calcium ions from being formed as LIME on concrete surface and improve the appearance and durability of coating.

Superplasticizer RXSOL-67-6704-210 ( High Range Concrete Superplasticiser )  is a brown color sulphonated formaldehyde condensate and sulphonated naphthalene with new generation polymners based admixture for use as a Superplasticizing admixture or high ranger Water Reducerad mixture for all types of concrete. This is in conformation to IS Code 9103:1999. Also meets the requirement of ASTM C 494 & type G and IS 9103-2003,  Suitable for ready mix concrete plants, it is capable of high workability retention up to 2-3 hrs with set retarding effect that helps to produce flowing concrete in hot climates. Further, it assists in long distance transportation of concrete at tropical atmosphere.

This has been formulated to reduce water requirement and to provide excellent plasticity and higher slump for both horizontal and vertical applications. RXSOL-67-6704-210 is manufactured under stringent quality control to ensure uniform and superior performance.

RXSOL-67-6704-210 imparts strong dispersion in the concrete reducing the total water demand in the mix. The reduction in water content also helps to achieve high ultimate strength. This is also very much useful for concrete with free pouring and pumpable consistency. Cement content of the concrete can also be economized with RXSOL-67-6704-210 due to its high cement dispersion property.

Technical Bulletin

Description :::

Construction applications: SUPERPLASTICIZERS are used to reduce water in CONCRETE formulations. specially formulated organic plasticizer improves the workability of concrete, reducing water requirement and making the concrete stronger. It retards the setting of concrete so that transportation of RMC is not a problem. Benefits of these additives include improved strength, improved workability, improved durability of cement mixtures. This polymer mixture in cement mixtures control air pore content and prevent AGGLOMERATION of powders during the spray-drying process from the powder manufacturing and storage. Coating formulations with RXSOL-67-6704-210 containing polymers prevent calcium ions from being formed as LIME on concrete surface and improve the appearance and durability of coating.

Superplasticizer RXSOL-67-6704-210 ( High Range Concrete Superplasticiser )  is a brown color sulphonated formaldehyde condensate and sulphonated naphthalene with new generation polymners based admixture for use as a Superplasticizing admixture or high ranger Water Reducerad mixture for all types of concrete. This is in conformation to IS Code 9103:1999. Also meets the requirement of ASTM C 494 & type G and IS 9103-2003,  Suitable for ready mix concrete plants, it is capable of high workability retention up to 2-3 hrs with set retarding effect that helps to produce flowing concrete in hot climates. Further, it assists in long distance transportation of concrete at tropical atmosphere.

This has been formulated to reduce water requirement and to provide excellent plasticity and higher slump for both horizontal and vertical applications. RXSOL-67-6704-210 is manufactured under stringent quality control to ensure uniform and superior performance.

RXSOL-67-6704-210 imparts strong dispersion in the concrete reducing the total water demand in the mix. The reduction in water content also helps to achieve high ultimate strength. This is also very much useful for concrete with free pouring and pumpable consistency. Cement content of the concrete can also be economized with RXSOL-67-6704-210 due to its high cement dispersion property.

Application :::

Superplasticizer RXSOL-67-6704-210  is utilized to provide high workability to cement or aggregate mix without adding extra water. It assists in improving retention of high workability without excessive retardation of set. It is suitable to use in high temperature & can be easily transported for long distances.

RXSOL-67-6704-210 can be used in all type of ready-mix and precast concrete where durable concrete with low water-cement ratio, high strength and low permeability is specified and in applications where high slump flowable concrete is required.

• Specially formulated for RMC.
• Delays cement hydration process and retains slump, thereby helping in transportation of concrete.
• In all concrete work such as basement walls, underground and overhead tanks.
• In all RCC walls, pillars etc.
• Reduces water/cement ratio while maintaining same slump.
• Highly cost effective
• Improves strength of concrete and reduces shrinkage cracks.

DOSE :::

RXSOL-67-6704-210 dosage should be determined according to the job specific requirements. Dosage rate will vary depending on the temperature, type of
cement, percentage of supplementary cementitious material, fineness of sand and water content. RXSOL recommends that trial mixes are performed in order to establish the required dosage and a regular process control tests should be conducted in order to adjust the admixture dosage.

In general practice Normally dispensed at a rate of 0.7-1.5 Liters per 100kg of cement. The dosage can further be enhanced to 3.5% depending on climatic situations. In general practice RXSOL-67-6704-210 added to the concrete with gauging water. ( It helps in reduction of water – cement ratio for the same slump. The required quantity of RXSOL-67-6704-210 is added to the concrete mix along with the water. )

The optimal dosage is determined by site trials.

It may also be added separately to freshly mixed concrete
It should be preferably added directly to water prior mixing to the wet aggregate
However, actual site trials should be conducted for finding exact dosages

(An indicative example: With control slump of 50 mm collapsible slum can be achieved for 15-30 min, 1 hr/170mm, 2 hr/150 mm &3hr120 mm depending on temperature & humidity condition with admixture dosage of   0.7% of the wt. of cement). Dosage may be increased or decreased depending upon slump required, humidity conditions, temperature & mix design. The above example is just for indication

Note: Example not rephrased.

NOTE :::— RXSOL-67-6704-210 can be added to the concrete mix near the end of mixing cycle in the concrete mixer and it can be also added on job-site by mixing at a higher speed and more revolutions in the truck.

It provides good cohesive pump able mix at low W/C ratio & moderate cement contents
 Imparts extreme fluidity to the concrete, which facilitates rapid placement of concrete
 Helps in controlled & predictable retardation of setting with improved slump retention
 Useful in production of self compacting concrete
 Provides high and extended slump suitable for  Better slump retention.
 Improves workability and plasticity
 Compatible with all types of cement.
 Reduces water requirement,increases strength and produce durable and dense concrete
 Improves pumping and finishing characteristics
 Reduces segregation
 Applied in complicated formwork or with congested reinforcement
 Achieves good compaction without any excessive vibration
 Reduced permeability, segregation and bleeding
 helps in increasing compressive and flexural strength
 It is chloride – free
Helps to achieve pumping concrete.
Increases ultimate strength with maximum water reduction.
Controls set retardation with optimum dosage.
Economizes the mix reducing cement content.
 

Technical Specification :::

Phase            Polymer Liquid
Type               Modified Naphthalene Formaldehyde Sulphonate And  2-Acrylamido-2-methylpropane sulfonic acid

Sp. Gravity    1.21
Shelf Life      1 Yr
Ph                  7-8
Chloride content  : Nil
Air content : < 1% Storage
RXSOL-67-6704-210 should be stored in dry and ventilated area at temperature above 0° C. If material is frozen please contact us. Shelf life is 1 year when stored in dry conditions between 10° C to 25° C in original unopened packages.

Technical Support
Our expert representative is available to assist in setting up the dosage and to address any concrete problems at plant or on-site.
 

RXSOL-67-6704-210 is for industrial use only and should be kept out of reach of children. This is non-toxic, non-flammable and non hazardous. However, any splash on the human body should be washed out immediately with plenty of water.

Product Label

Superplasticizer RXSOL-67-6704-210 ( High Range Concrete Superplasticiser ) is a new generation polymners based admixture for use as a Superplasticizing admixture or high ranger Water Reducerad mixture for all types of concrete. Suitable for ready mix concrete plants, It is capable of high workability retention up to 2-3 hrs with set retarding effect that helps to produce flowing concrete in hot climates. Further, it assists in long distance transportation of concrete at tropical atmosphere.
This has been formulated to reduce water requirement and to provide excellent plasticity and higher slump for both horizontal and vertical applications. RXSOL-67-6704-210 is manufactured under stringent quality control to ensure uniform and superior performance.
RXSOL-67-6704-210 imparts strong dispersion in the concrete reducing the total water demand in the mix. The reduction in water content also helps to achieve high ultimate strength. This is also very much useful for concrete with free pouring and pumpable consistency. Cement content of the concrete can also be economized with RXSOL-67-6704-210 due to its high cement dispersion property.